||Hose shall be made from 100% high tenacity synthetic yarn circular woven and completely,
protected by extruded through the weave synthetic rubber, forming a single homogenous construction without the
use of glues or adhesives of any type.|
||a. Ultimate Tensile Strength:|
Tensile strength of the lining and cover shall not be less than 1750 psi (12,000 k Pa ).
b. Ultimate Elongation:
450 % minimum.
||In very extreme conditions where abrasion is the most serious concern OROFLEX 20 would extend hose life.
Hose should have excellent abrasion resistance when tested with TABER abraser Wheel H-18 and 1000gr load.|
||- 22°F (-30°C) to 176°F(+80°C)|
||Hose shall show no visible signs of cracking of the lining or cover when tested in accordance with ASTM D1149-
64 (R1970), ASTM D518 Procedure B, 100pphm/118 F/70 hours.|
||Exposure to seawater and contamination by most chemical substances, hydrocarbons, oils, alkalis, acids and
greases must have no effect on the short or long term performance of the hose. A chemical resistance chart is
available and TIPSA will supply specific chemical resistance data on request of purchaser for unique applications.|
||The hose when subjected to a static pressure of 100 psi ( 700 k Pa ) shall be capable of withstanding a surface
temperature of 1112 F ( 600°C) (for a minimum of two minutes without rupture or damage to the synthetic
||Cover damage, small holes and punctures are repairable with use of REPOKIT and Vulcanizer. Full
instructions for use supplied on request.
||Standard 50’ (15m), 100’ (30m), 200’ (60m). special lengths up to 660’ (200m)
* Working Pressure can be raised up to 200 psi (14 bar) for short term periods.